Why Glass Fiber Reinforcement?
Adding glass fiber to nylon dramatically improves mechanical properties, making it suitable for demanding applications that unreinforced nylon cannot handle.
Property Improvements
| Eigentum | PA6 | PA6 + 30% GF |
|---|---|---|
| Zugfestigkeit | 75 MPa | 150 MPa |
| Biegemodus | 2,8 GPa | 7.5 GPa |
| HDT (1.8 MPa) | 70°C | 205°C |
| Feuchtigkeitsabsorption | 8% | 1.5% |
Anwendungen
- Automotive: radiator end tanks, intake manifolds
- Electrical: high-temperature connectors
- Industrial: pump housings, valve bodies
Processing Guidelines
- Dry at 80-100°C for 4-6 hours
- Use wear-resistant screw
- Higher mold temperatures (60-90°C)
FAQ
How do you know whether Glass Fiber Reinforced Nylon — When Standard Isn’t Enough fits a part?
Glass Fiber Reinforced Nylon — When Standard Isn’t Enough fits a part when its load capacity, temperature range, moisture exposure, wear behavior, and processing method match the real service conditions.
What properties should be checked for Glass Fiber Reinforced Nylon — When Standard Isn’t Enough?
Prüfen Sie Festigkeit, Steifigkeit, Schlagfestigkeit, Hitzebeständigkeit, Feuchtigkeitsaufnahme, Formstabilität, Reibung, Verschleiß und chemische Verträglichkeit.
What is the biggest selection risk for Glass Fiber Reinforced Nylon — When Standard Isn’t Enough?
Das größte Risiko besteht darin, sich auf einen Wert aus dem Datenblatt zu verlassen, ohne die tatsächlichen Umgebungsbedingungen, das Verarbeitungsverfahren, die Bauteilgeometrie und die langfristige Nutzung zu berücksichtigen.
When should Glass Fiber Reinforced Nylon — When Standard Isn’t Enough be tested before production?
Prüfungen werden empfohlen, wenn das Bauteil Belastungen, Hitze, Chemikalien, Feuchtigkeit, engen Toleranzen, gesetzlichen Anforderungen oder einer neuen Betriebsumgebung ausgesetzt ist.